Satin Polish Plaster

Description; Aralçı Satin Polish Plaster is a construction material where the high quality natural gypsumstone is cooked under suitable conditions, the seperation process is implemented and prepared with the appropriate implementation..

Practice Areas

• It can be applied to bricks, gas concrete,
concret, dirty and painted surfaces.

Features

• It is a kind of plaster that can easily be applied
  to Brick, concrete, concrete and concrete
  type bims surfaces with increased gypsumbased
  heat and sound insulation properties.
  • It covers the spaces and faults on the surfaces.
  It provides a platform that is like a glass and any
  kind of paint and decorative coverings can be
  applied on.
  • It provides a faultless and hard surface with its
  special particular despersal.
  • It can easily be applied due to its density.
  • It creates a healthy environment by balancing
  the moisture since it is a breathable material.
  • A flammable construction material.
  • Bacteria and fungus do not occur.

Surface Preperation


• The surfaces Aralçı Jointing Plaster is to be
  applied should be purified from dust, dirt, oil,
  etc. that prevent the hold.

Application Instructions

•Water used and the equipment should be
observed in terms of cleanness.
• The water used in the mixture should be
clean.
• The mortar should be prepared a rate of 10 kg
Aralçı Jointing Plaster into 6.5- 7 litres of water.
• Water is poured into the container and then
Aralçı Satin Plaster is added. 2-3 minutes are
waited for the plaster to absorb the water.
• The plaster is mixed until homogenous consistency
is achieved by mixing with a trowel or
hand mixer.
• If mechanic mixer is used in the mixing operation,
it should be done at a low speed.
• Water or gypsum should not be added to the
plaster after the mixing operation to prevent
the plaster clump.
• The materials to be used in the application
should be observed.
• Any other product or material should not be
added to Aralçı Satin Polish Plaster.
• Shaving and surface correction operations are
done after the plaster is hardened by a
• The mortar ready for the application is applied
by suppressing on the surface by a trowel. The
marks are removed by the steel trowel after the
plaster gets hardened.
• The plaster is rubbed down when it dries..

Warnings

Mixture of water / plaster ratio must be observed.
Otherwise, this ratio degradation spills,
may lead to cracking and decrease in strength.
• The application should not be done in very
warm, dry and windy weather conditions. •
• Applications to be done under very warm
weather conditions may result in spilled, fissures
and strength loss.
• Product storage terms should be observed.
• The products should not be preserved in
humid and very hot conditions.
• The products should not be preserved in
humid and very hot conditions.
• In case of ossification in bags, the products
should not be used.
• The powder should not be breathed since it
contains various chemical additives and plaster.
• It should not be in contact with skin and
eyes. In case of contact the skin and the eyes
should be washed with water. Masks, gloves
and working suits should be worn during the
studies.

Storage Conditions

• Aralçı Satin Polish Plaster bags should be
placed on top of a maximum of 18 bags in
a dry environment. Bags will not come into
contact with the ground, must be stored to
protect them from moisture. In these circumstances
Aralçı Jointing should be used within
9 months after the production date. Improper
storage conditions or exceeding the duration
of use can disrupt the quality of the product.

Package

• 30 kg polypropylene laminated bag.

Technical Properties:	(23° C and %50 Relative humidity)
General Information
Outlook	:White powder
Shelf Life	9 months indryenvironment inunopenedpackage
Application Information
Application Heat	: (+5° C) – (+35°C)
Mixage Ratio	: 1 kg/m2 (for 1 mm thickness)
Performace Information
Usage Time	: 100 minutes
Freezing Time	: 200 minutes
Bending Resistance	: ≥ 1 N/mm² (7 days)
Compression Strength	: ≥ ≥ 2 N/mm²
Dry Surface Rigidity	: ≥ 50 SHORE D
Standart	: TS EN 13279 -1 - C6/20/2